Welcome to the official website of Baoding Taichang Insulation Material Co., Ltd.!
1. Usage description
2601A/B environmental protection series room temperature curing epoxy resin can be used for the iron core of dry-type transformers. Good insulation performance, good process performance and excellent surface gloss. It is an excellent epoxy coating for covering transformer cores.
2. Appearance and characteristics
Component | Main agent 2601A | Hardener 2601B |
Colour | Black | Brown or transparent liquid |
Viscosity 40℃(mpa.s) | 3.0~4.0×104 | 180~270 |
Density 40℃(g/cm3) | 1.55~1.65 | 1.10~1.20 |
3. Mixing ratio
A:B=4:1
Usable time: 30-40 minutes at 25℃ (mixed amount 100g)
Curing conditions: The surface can be dried in 4 hours at 25℃, and can be cured in 24 hours. As the ambient temperature changes, the curing time period will change accordingly.
4.The operation process
1. Clean the surface of the iron core;
2. Stir 2601A evenly. After adding 2601B in proportion, fully stir A and B materials with a stirrer. The stirring time is 5-7 minutes. After the A and B materials are evenly mixed, they can be used.
5.Characteristics after curing
Compressive strength(kg/cm2) | 20~23 |
Bending strength(kg/cm2) | 10~12 |
Tensile strength(kg/cm2) | 16~18 |
Hardness(Shored) | 78~85 |
25℃ volume resistance(Ω/cm) | 1015 |
25℃ time surface resistance(Ω/cm) | 1014 |
6.Packaging
A: 24kg B: 6kg
7. Shelf life and conditions
Dry and ventilated place (shelf life: 180 days)
8. Matters needing attention
The activation period of this product is 40-50 minutes, please prepare it for immediate use. The unused product must not be poured into the unmixed product. It is normal that there may be a little precipitation during storage, please stir well before use.